Martensitic 1.4418 X4CrNiMo16-5-1 Stainless Steel Round Bar
Grade EN 1.4418, DIN X4CrNiMo16-5-1 with low carbon content is
popular with fabricators
as they are easier to weld than standard stainless martensitic
steels.
Martensitic 1.4418, X4CrNiMo16-5-1 achieve a strength level
comparable in some cases
to engineering steels, with a corrosion resistance that is close to that of well
known stainless EN 1.4301, AISI 304.
| Grade | C | Cr | Ni | Mo |
| 1.4418, X4CrNiMo16-5-1 | 0.04 | 16.00 | 5.00 | 1.00 |
Stainless EN 1.4418 grade combines the following characteristics:
- Best pitting corrosion resistance of all martensitic stainless
steel grades approaching that of 304
- Good strength. 700 MPa 0.2%PS, 900 MPa UTS at room temperature
- Excellent toughness, 80 J at room temperature. 40 J at -20°C
- Good weldability, especially for a martensitic stainless steel. No
preheating required.
- Post weld tempering recommended
- Good wet abrasion resistance
EN 1.4418 stainless grade is designed to achieve a good balance of
corrosion resistant and mechanical properties.
The chromium and molybdenum provides corrosion resistance.
The low carbon and increased nickel content provides a high
strength martensitic structure but with good toughness.
There are also significant amounts of austenite and ferrite in the
steel.
This structure also gives a much improved weldability compared to
normal higher carbon martensitic grades.
It is proving to be a replacement for stainless grade 431 (1.4057,
X17CrNi16-2) in some applications.
Applications which illustrate these features include:
Mining, cement plants, hydrofoil legs, anti-seismic applications,
helicopter landing grids, penstocks, hydroelectric
turbine blades, hardboard and chipboard press plate, propeller
shafting, pulp and paper.
For Details, please Contact
WUXI GUANGLU Special Steel Co., Ltd.
Stainless martensitic • precipitation hardening steel • stainless
ferritic — Our answer to your needs
Tel: +86 510 81812873
Email: export@guanglusteel.com