AISI 420 UNS S42000 Hot Rolled Stainless Steel Round Bars
We produce high performance stainless steel bar in martensitic,
precipitation hardening steels and ferritic grades.
Products available in forms of hot rolled/forged, cold drawn.
AISI 420, UNS S42000 Stainless Steel - a modification of AISI 410,
S41000 with a higher carbon content to
increase hardness, improve strength and give better wear resistance. 420 type of
stainless maintains its best
corrosion resistance in the heat treated condition.
It contains a minimum of 12 percent chromium, sufficient to give
420 stainless corrosion resistance properties.
It has good ductility in the annealed condition but is capable of
being hardened up to 55 RHC.
Its best corrosion resistance is achieved when 420 is hardened and
surface ground or polished.
In the hardened condition, 420 has good corrosion resistance to the
atmosphere, foods, fresh water, mild alkalies
and acids, steam, sterilizing solutions, crude oil, gasoline, and
other similar corrosive media.
420 is not recommended for use in temperatures above the relevant
tempering temperature,
because of reduction in mechanical properties. Principal
applications include Bushings, Dental and
Surgical Instruments, Pump Parts, Valve Parts, and Shafts.
General speaking, According to its carbon content, AISI 420
stainless family contains five types.
| Grade | Typical chemical composition |
| AISI 420A | C 0.16~0.25, Cr 12.00~14.00 |
| AISI 420B | C 0.26~0.35, Cr 12.00~14.00 |
| AISI 420X | C 0.36~0.42, Cr 12.50~14.50 |
| AISI 420C | C 0.43~0.50, Cr 12.50~14.50 |
| AISI 420D | C 0.58~0.70, Cr 12.50~14.50 |
| Condition | Dia. ( Shap, round bar ) |
| Hot rolled | 14.0~130.0mm |
| Hot forged | 60.0~450.0mm |
| Cold drawn | 0.3~16.0mm |
| Surface in black, peeled, polished, ground |
For Details, please Contact
WUXI GUANGLU Special Steel Co., Ltd.
Stainless martensitic • precipitation hardening steel • stainless
ferritic — Our answer to your needs
Tel: +86 510 81812873
Email: export@guanglusteel.com