Material FV520B Stainless Steel Round Bars Grade 1.4594
X5CrNiMoCuNb14-5
FV520B is a martensitic precipitation hardening stainless steel.
It combines moderate corrosion resistance with high strength and
moderate toughness.
| Brand | EN/DIN | Chemical composition % |
| FV520B | 1.4594 X5CrNiMoCuNb14-5 | C 0.07, Si 0.7, Mn 1.0, P 0.035, S 0.025, Cr 13.2~14.7, Ni 5.0~6.0,
Mo 1.2~2.0, Nb 0.2~0.7, Cu 1.2~2.0 |
FV520B stainless grade combines the following characteristics:
- Moderate corrosion resistance, better than standard martensitic
grades.
- Can be better than 17-4 PH depending on environment
- Controlled balance of mechanical properties by ageing
(precipitation hardening)
- High 0.2% proof strength from 720 MPa minimum to 1030 MPa minimum
dependent on heat treatment condition
- Moderate toughness – 40 Joules minimum in lowest heat treatment
condition even at moderately low sub-zero
- temperatures –70°C
- Weldable with matching consumables
- Difficult to machine
FV 520B, like 17-4 PH, develops its high strength from the
precipitation of copper particles in its martensitic matrix.
The supply of this grade is complicated by the mismatch between the
“traditional” heat treatment conditions
and those laid down in the EN standard. For example, age hardening at
450°C has long been considered
to give the maximum strength in this grade. Yet, no such heat treatment is
recognised in EN 10088-3.
The aerospace standards S143/144/145 are closer to established heat
treatments.
The combination of high strength and good corrosion resistance
finds uses in:
Pump shafts, impellers, fasteners, fans, valves, hydraulic
equipment, turbine blades, aerospace,
nuclear transport flask, medical devices.
We supply FV520B, 1.4594 / X5CrNiMoCuNb14-5 stainless steel round
bars, plates / sheet, forgings.
For Details, please Contact
WUXI GUANGLU Special Steel Co., Ltd.
Stainless martensitic • precipitation hardening steel • stainless
ferritic — Our answer to your needs
Tel: +86 510 81812873
Email: export@guanglusteel.com