17-4PH 630 Stainless Steel Bright Round Bars And Wire In Rods
Straightened
Precipitation hardening stainless steel 17-4PH, S17400, AISI 630,
EN 1.4542, DIN X5CrNiCuNb16-4
17-4PH is a chromium-nickel-copper precipitation hardening
stainless steel used for applications requiring
high strength and a moderate level of corrosion resistance. High
strength is maintained to approximately 600°F (316°C).
The 17-4PH alloy is martensitic in structure in the annealed
condition and is further strengthened by a
low temperature treatment which precipitates a copper containing
phase in the alloy.
In comparison to many alloys in the precipitation hardening family,
material 17-4PH requires a simple
heat treatment; a one step process conducted at a temperature in the range 900°F
(482°C) to 1150°F (621°C)
depending on the combination of strength and toughness desired.
A wide range of properties can be produced by this one step heat
treatment.
Heat treatment in the 900°F (482°C) range produces highest
strength.
Chemical composition % weight
| C | Si | Mn | P | S | Cr | Ni | Cu | Nb |
| 0.07 | 1.00 | 1.00 | 0.040 | 0.030 | 15.5~17.5 | 3.00~5.00 | 3.00~5.00 | 0.15~0.45 |
Forms of supply
We produce 17-4PH, 630 Stainless steel bars, round, flat, square
shapes.
products in hot rolled, forged, cold drawn condition.
We also produce 17-4PH stainless in sheet, strip, and plate product
forms.
17-4PH is produced in compliance with aerospace specifications such
as AMS 5604 and standard
industrial specifications such as ASTM A693 and ASME SA-693.
For Details, please Contact
WUXI GUANGLU Special Steel Co., Ltd.
Stainless martensitic • precipitation hardening steel • stainless
ferritic — Our answer to your needs
Tel: +86 510 81812873
Email: export@guanglusteel.com